Test Standards for the Q-FOG Cyclic Corrosion Tester
ASTM B117
Standard Practice for Operating Salt Spray (Fog) Apparatus
This practice provides a controlled corrosive environment which has been utilized to produce relative corrosion resistance information for specimens of metals and coated metals exposed in a given test chamber.
ASTM D1654
Voluntary Specification, Performance Requirements and Test Procedures for High Performance Organic Coatings on Aluminum Extrustions and Panels
This specification describes test procedures and performance requirements for high performance organic coatings applied to aluminum extrusions and panels for architectural products.
ASTM D1735
Standard Practice for Testing Water Resistance of Coatings Using Water Fog Apparatus
This practice covers the basic principles and operating procedures for testing water resistance of coatings in an apparatus similar to that used for salt spray testing.
ASTM D2247
Standard Practice for Testing Water Resistance of Coatings in 100% Relative Humidity
This practice covers the basic principles and operating procedures for testing water resistance of coatings by exposing coated specimens in an atmosphere maintained at 100% relative humidity so that condensation forms on the test specimens.
ASTM D2803
Standard Guide for Testing Filiform Corrosion Resistance of Organic Coatings on Metal
This guide covers three procedures for determining the susceptibility of organic-coated metal substrates to formation of filiform corrosion.
ASTM D3451
Standard Guide for Testing Coating Powders and Powder Coatings
This guide covers the selection and use of procedures for testing coating powders and powder coatings. The test methods included are listed in Table 1. Where more than one test method is listed for the same characteristic, no attempt is made to indicate superiority of one method over another. Selection of the methods to be followed must be governed by experience and the requirements in each individual case, together with agreement between the purchaser and the seller.
ASTM D4585
Standard Practice for Testing Water Resistance of Coatings Using Controlled Condensation
This practice covers basic principles and operating procedures for testing water resistance of coatings using controlled condensation.
ASTM D5894
Standard Practice for Cyclic Salt Fog/UV Exposure of Painted Metal, (Alternating Exposures in a Fog/Dry Cabinet and a UV/Condensation Cabinet)
This practice covers basic principles and operating practice for cyclic corrosion/UV exposure of paints on metal; using alternating periods of exposure in two different cabinets: a cycling salt fog/dry cabinet, and a fluorescent UV/condensation cabinet.
ASTM D6577
Standard Guide for Testing Industrial Protective Coatings
This guide covers the selection and use of test methods and procedures for testing industrial protective coatings.
ASTM D6675
Standard Practice for Salt-Accelerated Outdoor Cosmetic Corrosion Testing of Organic Coatings on Automotive Sheet Steel
This practice is designed to assist procedures to be followed when conducting outdoor exposures to evaluate cosmetic corrosion that might occur in steel panels covered with an organic coating that has been damaged.
ASTM G85
Standard Practice for Modified Salt Spray (Fog) Testing
This practice covers and sets forth conditions for five modifications in salt spray (fog) testing for specification purposes.
BS 2011 Pt2.1 Ka
Test KA Salt Mist
See ISO 60068-2-11
BS 2011 Pt2.1 Kb
Test KB. Salt Mist, Cyclic (Sodium Chloride Solution)
See ISO 60068-2-52
BS 3900 F12
Methods of Test For Paints - Part F12: Determination of Resistance to Neutral Salt Spray (FOG)
See ISO 7253
BS 5466 1
Methods For Corrosion Testing of Metallic Coatings Part 1: Neutral Salt Spray Test (NSS TEST)
See ISO 9227
BS 7479
Method For Salt Spray Corrosion Tests in Artificial Atmospheres
See ISO 9227
DIN 50017
Condensation Water Tests Atmospheres
See ISO 6270
DIN 50021
Salt Spray Testing
See ISO 9227
Ford CETP 00.00-L-467
Global Laboratory Accelerated Cyclic Corrosion Test
This standard specifies an accelerated laboratory atmospheric corrosion test.
Ford FLTM BI 103-01
Salt Spray Resistance Test for Painted Panels and Parts
This method is used to test the resistance to salt spray of painted panels and parts.
Ford FLTM BI 104-01
Water Immersion Test for Painted Parts and Panels
This method is used to determine the resistance to failure of painted metal and painted plastic parts and representative test panels when immersed in water.
Ford FLTM BI 104-02
Condensing Water Vapor Test
This procedure is used to evaluate the effects of a condensing water atmosphere on treated panels.
Ford FLTM BI 123-03
Component Corrosion Test
This test procedure is used to evaluate the corrosion performance of coatings applied to components. It is designed to simulate the corrosive conditions of the Arizona Proving Ground (APG) Vehicle Accelerated Corrosion Test (CETP 00.00-R-311).
Ford FLTM BQ 105-01
Copper-Accelerated Acetic Acid-Salt Spray Testing (CASS Test)
This procedure is used to determine the corrosion resistance primarily of stainless steel and plated parts. With respect to plated parts, it is used primarily for copper/nickel/chromium and nickel/chromium electroplated parts.
GB 5938
corrosion-resistant testing method of the metal deposits and conversion coatings for the light industrial products Neutral salt spraying test (NSS)
This standard applies to the inspection of the corrosion resistance of metal coatings and chemically treated layers.
GB/T 10125
Corrosion tests in artificial atmospheres-salt spray tests
This standard specifies the equipment, reagents and methods used for neutral salt spray (NSS), acetate salt spray (AASS), and copper-accelerated acetate salt spray (CASS) tests.
GB/T 1771
Paints and varnishes-determination of resistance to neutral salt spray (fog)
This standard specifies the method for determining the resistance of coatings to neutral salt spray.
GB/T 20853
Corrosion of metals and alloys-Corrosion in artificial atmosphere-Accelerated corrosion test involving exposure under controlled conditions of humidity cycling and intermittent spraying of a salt solution
This standard specifies the test method for the corrosion resistance of metals in the presence of chloride ions. Chloride ions are mainly sodium chloride from marine and highway deicing salts.
GB/T 20854
Corrosion of metals and alloys-Accelerated testing involving cyclic exposure to salt mist, "dry" and "wet" condition
This standard specifies the instruments and test methods for accelerated corrosion tests used to evaluate the corrosion resistance of metal materials used in outdoor salt-contaminated environments, regardless of whether the material being tested has permanent or temporary corrosion protection. This standard specifies the conditions for cyclic exposure of samples to neutral salt spray, "dry" and "wet" test environments.
GM 4298P
Salt Spray Test
GM 4465P
Water Fog Humidity Test
This standard covers the requirements for testing water resistance of coated specimens in saturated water fog conditions.
GM 9540P
Accelerated Corrosion Test
This procedure describes an accelerated laboratory corrosion test method to evaluate assemblies and components. The test procedure provides a combination of cyclic conditions (salt solution, various temperatures, humidity, and ambient environment) to accelerate metallic corrosion.
GMW 14729 (Option A)
Procedures For High Humidity Test
This procedure describes two options (water fog and wet-bottom) of high humidity testing which are typically used to evaluate the influence of high humidity environments to coated substrates. This influence is usually measured by testing physical and mechanical properties before and after exposure.
GMW 14872
Cyclic Corrosion Laboratory Test
This procedure describes an accelerated laboratory corrosion test method to evaluate assemblies and components. The test procedure provides a combination of cyclic conditions (salt solution, various temperatures, humidity, and ambient environment) to accelerate metallic corrosion.
GMW 3286
Neutral Salt Spray (NSS) Test
The neutral salt spray test is typically used to evaluate the corrosion resistance of metallic substrates and the corrosion preventative properties of coatings.
Honda HES D6001 sec 4.3
General Test Methods For Plating
This standard specifies general test methods for plating.
Honda HES D6501 sec 3.15.1
General Test Methods For Coating
This procedure describes a salt spray test.
Honda HES D6501 sec 3.15.2
General Test Methods For Coating
This procedure describes a filiform corrosion test.
IEC 60068-2-11
Basic Environmental Testing Procedures, Part 2: Test KA: Salt Mist
This test is to be applied to compare the resistance to deterioration from salt mist of specimens of similar construction. It is useful for evaluating the quality and the uniformity of protective coatings.
ISO 16701
Corrosion of Metals and Alloys - Corrosion in Artificial Atmosphere - Accelerated Corrosion Test Involving Exposure Under Controlled Conditions of Humidity Cycling and Intermittent Spraying of Salt Solution
This International Standard defines an accelerated corrosion test method to be used in assessing the corrosion resistance of metals in environments where there is a significant influence of chloride ions, mainly as sodium chloride from a marine source or from road de-icing salt.
ISO 60082-2-52
Environmental Testing - Part 2: Tests - Test KB. Salt Mist Cyclic (Sodium Chloride Solution)
Specifies a test for components or equipment designed to withstand a salt-laden atmosphere. To be read in conjunction with BS EN 60068-1:1995.
ISO 6270-2
Paints And Varnishes - Determination of Resistance to Humidity - Part 2: Procedure For Exposing Test Specimens in Condensation- Water Atmospheres
This part of ISO 6270 describes the general conditions and procedures which need to be observed when testing coated test specimens in constant condensation-water atmospheres or in alternating condensation water atmospheres.
ISO 7253
Paints and Varnishes- Determination of resistance to neutral salt spray (fog)
This International Standard is one of a series of standards dealing with the sampling and testing of paints, varnishes and related products.
ISO 9227
Corrosion Tests in Artificial Atmospheres - Salt Spray Tests
JIS H8502 Se. 7.3
Methods of Corrosion Resistance Test for Metallic Coatings
This standard specifies the methods of corrosion resistance testing for the metallic coatings and products coated with metal.
JIS Z2371 Sect. 7.2.3
Methods of Salt Spray Testing
This Japanese Industrial Standard specifies the required apparatus, reagent, technique or acceptance criteria when testing the corrosion resistance of metallic materials, or of those electroplated or treated with inorganic or organic films by the methods of neutral salt spray test (NSS), acetic acid salt spray test (AASS), or CASS test (CASS).
Mazda MES MN601
Test Method for Paint Films
This MES specifies a test method for coating films applied to automotive parts for the main purpose of corrosion prevention and ornamentation.
Mazda MES MN601, MCT-2M
Test Mode for Corrosion Resistance Test
This procedure describes a salt spray test.
Mazda MES MN601, MCT-3M
Test Mode for Corrosion Resistance Test
This procedure describes a salt spray test.
MIL-STD-202 (101E)
Test Method Standard: Electronic and Electrical Component Parts
The salt-spray test, in which specimens are subjected to a fine mist of salt solution, has several useful purposes when utilized with full recognition of its deficiencies and limitations.
Renault ECC1 - D17 2028
Corrosion Test by Automatic Phase Change Salt Spray Humidity and Drying
This test method is intended to describe a cycle of the cyclic corrosion test 1 (Essai de Corrosion Cyclique 1: ECC1) on the associated equipment and the verifications which are necessary to make sure that the test is in conformity.
SAE J1959
Corrosion Preventive Compound, Underbody Vehicle Corrosion Protection
SAE J2334
Laboratory Cyclic Corrosion Test
The SAE J2334 lab test procedure should be used when determining corrosion performance for a particular coating system, substrate, process, or design. Since it is a field-correlated test, it can be used as a validation tool as well as a development tool. If corrosion mechanisms other than cosmetic or general corrosion are to be examined using this test, field correlation must be established.
T/CSAE 71
Cyclic corrosion test methods of automotive assemblies and materials
This standard specifies the cyclic corrosion test methods for automotive parts and materials.
Toyota TSH 1555G
Test Method For Accelerated Corrosion Under Complex Environment
This standard covers the test method for reproduction, at an accelerated pace, of corrosion on each part of a vehicle body, in order to simulate the corrosion produced on actual vehicles.
Volvo STD 1027,1375
Accelerated Atmospheric Corrosion Testing – Volvo Indoor Corrosion Test (VICT)
This standard concerns determination of atmospheric corrosion resistance in an accelerated test. The test method has been developed to simulate the corrosion processes that take place on vehicles in a road environment where sodium chloride constitutes a dominating corrosive component.
Volvo STD 423-0014
Accelerated Corrosion Test
This standard defines an accelerated corrosion test method to be used in assessing the corrosion resistance of metals in environments where there is a significant influence of chloride ions, mainly as sodium chloride from a marine source or by winter road deicing salt.
Volvo VCS 1027-14
Accelerated Corrosion Test
This standard defines an accelerated corrosion test method to be used in assessing the corrosion resistance of metals in environments where there is a significant influence of chloride ions, mainly as sodium chloride from a marine source or by winter road deicing salt.
Looking for a specific test standard? Search entire listing of all standards.
Agora você está logado na sua conta. Agora você pode acessar livremente todos (
) ou (
) documentos. Para acesso (
) documentos, registre seu equipamento aqui.
Agora você está logado na sua conta. Agora você pode acessar livremente todos () ou () documentos. Para acesso () documentos, registre seu equipamento aqui.